Home › Structural Steel › Q355D Steel Plate

Q355D STRUCTURAL STEEL PLATE

Chemical element composition – hot-rolled Q355D low-alloy high-strength steel 🔍 Q355D Grade Lookup →

Product Overview

Q355D is a Chinese grade low-alloy high-strength structural steel conforming to GB/T 1591-2018 standard. Grade D provides guaranteed impact toughness at -20°C. With minimum yield strength of 355MPa (≤16mm) and excellent low-temperature performance, it is widely used in bridges, buildings, vehicles, pressure vessels, and engineering structures requiring enhanced low-temperature service conditions. Q355D is the new designation that replaces the previous Q345D grade.

Equivalent grades: Q355D ↔ Q390D (higher strength domestic), S355J2 (EN 10025-2), S355D (ISO 630-2), ASTM A572 Gr.50 (USA).

International Grade Comparison

Europe (EN 10025-2)

S355J2

Impact: -20°C (27J)

Yield: 355MPa

C: ≤0.22%

Si: ≤0.55%

Mn: ≤1.60%

P: ≤0.025%

S: ≤0.025%

Nb: ≤0.05%

V: ≤0.12%

Ti: ≤0.05%

ISO 630-2

S355D

Impact: -20°C (27J)

Yield: 355MPa

C: ≤0.22%

Si: ≤0.55%

Mn: ≤1.60%

P: ≤0.025%

S: ≤0.025%

Nb: ≤0.05%

V: ≤0.12%

Ti: ≤0.05%

USA (ASTM A572)

Gr.50

Impact: Not specified

Yield: 345MPa

C: ≤0.23%

Si: ≤0.40%

Mn: ≤1.35%

P: ≤0.025%

S: ≤0.025%

Nb: ≤0.05%

V: ≤0.15%

Ti: ≤0.05%

China (GB/T 1591)

Q390D

Impact: -20°C (34J)

Yield: 390MPa

C: ≤0.20%

Si: ≤0.50%

Mn: 1.00-1.70%

P: ≤0.025%

S: ≤0.025%

Nb: ≤0.05%

V: ≤0.12%

Ti: ≤0.05%

China (GB/T 1591)

Q355D

Impact: -20°C (34J)

Yield: 355MPa

C: ≤0.20%

Si: ≤0.55%

Mn: ≤1.60%

P: ≤0.025%

S: ≤0.025%

Nb: ≤0.05%

V: ≤0.12%

Ti: ≤0.05%

Note: Q355D offers -20°C impact toughness comparable to S355J2 and S355D; always verify specific requirements before substitution.

China Grade Comparison: Q355B vs Q355C vs Q355D

Q355B

Grade B

Impact: 20°C

KV2 (L): 34J

C: ≤0.20%

P: ≤0.035%

S: ≤0.035%

Q355C

Grade C

Impact: 0°C

KV2 (L): 34J

C: ≤0.20%

P: ≤0.030%

S: ≤0.030%

Q355D

Grade D

Impact: -20°C

KV2 (L): 34J

C: ≤0.20%

P: ≤0.025%

S: ≤0.025%

Note: Q355 series grades share identical tensile properties (yield strength, tensile strength, elongation). The key differences are impact test temperature and corresponding impurity limits: B (20°C, 34J), C (0°C, 34J), D (-20°C, 34J), with progressively tighter P/S control for lower temperatures.

Key Advantages

Excellent Weldability

Low carbon content (≤0.20-0.22%) and low carbon equivalent ensure superior weldability without preheating for most thicknesses.

High Strength

Minimum yield strength of 355MPa (≤16mm) and tensile strength 470-630MPa, ideal for structural applications.

-20°C Impact Toughness

Guaranteed impact energy of 34J at -20°C (longitudinal), suitable for low-temperature service conditions.

Applications

Building Structures

High-rise buildings, industrial plants in cold regions

Heavy Machinery

Construction machinery, crane booms for arctic conditions

Q355D Chemical Composition (GB/T 1591-2018)

Grade C (≤40mm) C (>40mm) Si Mn P S Cr Ni Cu N
Q355D ≤0.20 ≤0.22 ≤0.55 ≤1.6 ≤0.025 ≤0.025 ≤0.3 ≤0.3 ≤0.4 ≤0.012

Notes: a. For thickness >100mm, carbon content negotiable. b. For thickness >30mm, carbon ≤0.22%. c. For structural steel and bars, P/S upper limit may increase by 0.005%. d. The maximum percentage for Q390/Q420 can reach 0.07%, for Q460 up to 0.11%. e. Up to 0.2%. f. If Als ≥0.015% or Alt ≥0.02%, nitrogen content not limited. g. Applicable only to structural steel and bars.

Q355D Mechanical Properties (GB/T 1591-2018)

Upper yield strength ReH/MPa ≥
Grade ≤16mm >16-40mm >40-63mm >63-80mm >80-100mm >100-150mm >150-200mm >200-250mm >250-400mm
Q355D 355 345 335 325 315 295 285 275 265*

* For thickness >250-400mm, applies only to quality grade D plates.

Tensile Strength Rm (MPa)

Grade ≤100mm >100-150mm >150-250mm
Q355D 470-630 450-600 450-600

Impact Energy KV2 at -20°C (J) min.

Grade Longitudinal Transverse
Q355D 34 27

Notes: a. When yield strength not obvious, use Rp0.2. b. Applicable only to steel plates of quality grade D. c. Applicable only to structural steel and bars.

Size & Specification

Product Form Thickness (mm) Width (mm) Length (mm)
Plate 3 - 300 1000 - 4000 3000 - 18000
Sheet / Coil 1.5 - 20 900 - 2000 Coil or cut to length

Other sizes available. Tolerances per GB/T 709.

Customizable Options

We offer comprehensive customization services to meet your specific project requirements:

Custom Dimensions
Non-standard sizes, laser cutting		 Surface Treatments
Shot blasting, priming		 Edge Preparation
Beveling, machining
Custom Heat Treatment
Normalizing, stress relieving		 Special Testing
Third-party inspection		 Custom Marking
Special labeling

Quality & Manufacturing Assurance

Modern Production

Advanced continuous casting and controlled rolling

In-process Inspection

Spectral analysis, mechanical testing, -20°C impact

Full Documentation

Mill Test Certificate EN 10204 3.1

Packaging & Logistics

  • Packaging: Steel plates bundled with steel straps on wooden skids. Coils wrapped with waterproof paper.
  • Marking: Each bundle marked with grade, size, heat number, weight.
  • Logistics: FOB, CIF, CFR from main Chinese ports. Lead time 25-35 days.

Request a Quote

Emails go directly to customize@cehesteel.com — reply within 2h.

Frequently Asked Questions

Carbon content? ≤0.20% for ≤40mm and ≤0.22% for >40mm thickness.
Weldability? Excellent weldability due to low carbon equivalent (Ceq ≤0.45).
Thickness range? Available from 3mm to 300mm in standard plate form.
Q355C vs Q355D? Q355D offers -20°C impact while Q355C provides 0°C impact toughness.
Mill certificates? Yes, EN 10204 Type 3.1 or 3.2 available upon request.
MOQ? 5 tons for stock sizes, negotiable for mill production orders.